Bending moment capacity of round mortise and tenon furniture joints
(Forest Products Soc, 2004)
Tests were conducted to determine the effect of cross pinning the tenons of round mortise and tenon joints on the bending moment capacity of the joints. Tenon diameters ranged from a nominal 0.6 to 1.0 inches. Cross-pins ...
SOME SURFACE CHARACTERISTICS OF VARNISHED THERMOWOOD AFTER WEATHERING
(Slovak Forest Products Research Inst, 2019)
This study was designed to investigate some surface characteristics such as glossiness and surface roughness changes of varnished thermowood after six months of weathering. Thermal modification of Scots pine (Pinus sylvestris ...
Some combustion parameters of wood impregnated with borates
(Forest Products Soc, 2009)
This study was conducted to determine some of the combustion parameters of Calabrian pine and Oriental beech treated with borates. Average mass loss and temperature values of Calabrian pine and Oriental beech wood were ...
Effect of hole diameter, hole distance from the edge, and material properties on lateral pin holding strength of medium density fiberboard and particleboard
(Forest Products Soc, 2004)
There is no established standard which evaluates the lateral holding resistance of wood composites. The method of test offered in this study intends to determine the lateral resistance of panels used in case constructions ...
SOME PHYSICAL CHARACTERISTICS OF THERMALLY MODIFIED ORIENTAL-BEECH WOOD
(Univ Bio-Bio, 2014)
Heat treatment of Oriental-beech (Fagus orientalis) wood was carried out by hot air in an oven for 2, 4, and 8 h at 140, 170, and 200 degrees C. After heat treatment, some physical characteristics such as surface roughness, ...
Some mechanical properties of wood impregnated with environmentally- friendly boron and copper based chemicals
(Slovak Forest Products Research Inst, 2013)
The aim of this study was made to determine some mechanical properties such as compression strength parallel to grain (CSPG), modulus of rupture (MOR), and modulus of elasticity (MOE) of wood treated with some boron and ...
Increasing the physical and combustion performance of Oriental beech by impregnating borates and coating liquid glass
(ASSOC BRASIL POLIMEROS, 2021)
This study was designed to investigate physical properties such as color changes after weathering and water absorption (WA) levels, and combustion performance of borates-impregnated and LG-coated Oriental beech wood. Results ...
Improvement of technological properties of wood plastic composites reinforced with glass and carbon fibre fabric
(SAGE Publications Ltd, 2021)
In this study, HDPE-based flat-pressed WPCs were reinforced with glass fibre and carbon fibre woven fabrics, which could be used where high strength and stiffness are required. The effect of reinforcement on some physical, ...
COMPARISON OF SOME WOOD PROPERTIES OF JUVENILE BLACK PINES OF DIFFERENT ORIGIN PLANTED IN THE SAME HABITAT
(Universidad del Bio-Bio, 2021)
Black pine (Pinus nigra) is a significant raw material source for the forest products industry in Turkey. The purpose of this research was to study some chemical, anatomical, physical, and mechanical properties of wood ...
SOME SURFACE CHARACTERISTICS OF ORIENTAL BEECH WOOD IMPREGNATED WITH SOME FIRE-RETARDANTS AND COATED WITH POLYUREA/POLYURETHANE HYBRID AND EPOXY RESINS
(Universidad del Bio-Bio, 2021)
This study was made to determine surface characteristics such as colour, gloss, and surface hardness changes of Oriental beech (Fagus orientalis). The wood specimens were firstly impregnated with some fireretardants(FRs) ...