SURFACE CHARACTERISTICS OF SCOTS PINE TREATED WITH CHEMICALS CONTAINING SOME COPPER COMPOUNDS AFTER WEATHERING
Özet
In this study, it was aimed to investigate surface hardness, gloss, and color changes of Scots pine treated with chemicals containing some copper compounds after six months weathering. Adolit KD-5 (AD KD-5), celcure AC-500 (CAC-500), and wolmanit CX-8 (WCX-8) were used as impregnation chemicals containing copper compounds. Scots pine wood specimens were treated with 2 % aqueous solution of chemicals according to ASTM D1413-07e1 (2007) standard. Results showed that while surface hardness and gloss values of untreated Scots pine wood specimens were decreased after weathering, they increased treated Scots pine wood specimens after weathering. The decrease in L* of untreated and treated wood indicates that the specimens became darker after weathering. While weathering caused less green and less yellow for untreated control specimen, it caused less red and less yellow for treated wood. Treated Scots pine wood specimens showed better color stability compared to untreated Scots pine after weathering. In terms of surface hardness, gloss, and color stability values CAC-500 treated Scots pine gave the best results after weathering.