SYNTHESIS OF MAGNESIUM SILICATE FROM WHEAT HUSK ASH: EFFECTS OF PARAMETERS ON STRUCTURAL AND SURFACE PROPERTIES
Özet
In the present study, magnesium silicate was produced by using wheat husk ash. Wheat husk was burned at 600 degrees C to obtain an amorphous ash structure, and the ash was processed with sodium hydroxide solution with heat to extract silica. Sodium silicate solution and magnesium salts were used to synthesize magnesium silicate. The present study investigates effects of the feeding rate on magnesium silicate production (0.6 mL/min, 35 mL/min, 70 mL/min), the type of magnesium salt (MgSO4 center dot 7H(2)O or MgCl2 center dot 6H(2)O), temperature (25 degrees C or 50 degrees C), and the washing agent ( water and acetone) on the chemical composition and surface characteristics of magnesium silicate. The results demonstrated that all of the variables affected the surface characteristics of magnesium silicate, such as surface area, particle size, and pore volume. However, it was also observed that the studied parameters did not affect the chemical composition of magnesium silicate. The wheat husk ash-based magnesium silicates obtained in the experimental study had a BET surface area ranging from 79 to 91 m(2)/g and a particle size varying from 42 to 63 mu m.