Room-temperature five-tesla coercivity of a rare-earth-free shell-ferromagnet

Abstract

Ni2MnX-based Heusler (X: main group element), when enriched with Mn, will decompose into ferromagnetic Ni2MnX and antiferromagnetic NiMn when temper-annealed around 650 K. When the starting material is chosen such that the X-composition is about 5 at. % and the annealing takes place in the presence of a magnetic field of about 1 T, the resulting material is a composite of nanoprecipitate strongly pinned shell-ferromagnets with a soft ferromagnetic core embedded in the antiferromagnetic matrix. We show that the shells of the precipitates are so strongly pinned that the estimated field required to fully reorient the spins is in the order of 20 T. We examine in a Ni50.0Mn45.1In4.9 sample the pinning and the magnetic interactions of the precipitate and the matrix with magnetization and ferromagnetic resonance studies carried out in fields ranging up to 14 and 12 T, respectively. © 2017 Author(s).