Synthesis and Characterization of 2-Hydroxyethyl Methacrylate (HEMA) and Methyl Methacrylate (MMA) Copolymer Used as Biomaterial
Özet
A series of poly(methyl methacrylate-co-hydroxyethyl methacrylate) (PMMA-co-PHEMA), copolymers were synthesized by an emulsion polymerization technique. Copolymer compositions were determined by FT-IR and 1H-NMR spectroscopy. It was found that comonomer ratios used in the recipes were comparable within the actual copolymers. Glass transition temperatures (Tg) of PMMA-co-PHEMA copolymers were varied from 119 degrees C to 100 degrees C by increasing HEMA content. Thermogravimetric analysis showed that the copolymers were stable up to 330 degrees C. High intrinsic viscosity values of copolymer resulted in ductile solution-cast films. The hydrophilicity of the films was analyzed by water uptake measurements.
