The effect of different sputtering parameters on coating thickness and hardness in MoS(2)coated films with and without interlayer
Özet
The aim of this study is; to examine the effect of different sputtering parameters on coating thickness and hardness in MoS(2)films which are deposition of radio frequency (RF) magnetron sputtering method. Therefore, 440C steel substrates are coated with MoS(2)thin films which exhibit lubrication as a solid lubricant and low friction characteristic during shear. MoS(2)films with no interlayer and (Ti/Cr) with interlayer were deposited on the AISI 440C substrates. During the coating, by changing the deposition parameters such as the substrate deposition temperature and RF sputtering power, steel disc groups which are coated in 15 different deposition parameters were obtained. The thicknesses of the films were measured by using a SEM. The surface topographies were observed at different magnifications. The composition and structure were analysed by energy dispersive spectroscopy (EDS). A nano-indentation system was used to determine the hardness and elesticity modules of the coatings.